Shanghai Glass Ionomer Cement
Original price was: $ 18.75.$ 7.12Current price is: $ 7.12.
Advanced dental cement for strong, versatile, fluoride-releasing restorations
| Quantity | Price |
|---|---|
| 2 - 5 | $ 7.05 |
| 6 - 10 | $ 6.98 |
| 11 - 20 | $ 6.84 |
| 21 - 50 | $ 6.76 |
| 51 + | $ 6.62 |
Features
- Glass Ionomer formulation
- Fluoride release
- High mechanical strength
- Excellent wetting properties
- Film thickness of just 15 microns
- Radiopaque
- Sharp set characteristics
- Low solubility
- Long term clinical data.
Description
Glass Ionomer Cement is a dental material widely used for various applications in dentistry. It typically consists of a powdered component, which includes glass particles and various metal oxides, and a liquid component, usually an aqueous solution of polyacrylic acid. When mixed, these components form a cement that adheres well to tooth structures. GIC is valued for its unique properties, including fluoride release, adhesion to tooth tissues, biocompatibility, and radiopacity. It is commonly used for tasks such as filling cavities, cementing crowns and bridges and attaching orthodontic brackets. The material sets through an acid-base reaction and bonds chemically with the tooth structure.
- Shanghai Glass Ionomer cement is used in dentistry as a filling material and luting cement, including for orthodontic bracket attachment.
Advantages:
- Shanghai Glass Ionomer Cement for all types of cavities, inlays, onlays and cementation of crown and bridge.
- Highly biocompatible and nonirritant to the tissues.
- Excellent strength, good marginal seal, and is insoluble in the oral cavity.
- High flexural strength, reduces the risk of restoration fracture.
- Adhesion to enamel and dentin.
- Long-term fluoride release.
- Low acid erosion.
- Radiopaque.
- Cost-effective.
- Smooth Mixing.
- Delivery system – Hand-mixed.
- Product type – Cement
- Compressive Strength – High up to 200.
- Material –Radio-opaue .
- Cement Dispensing Form – Powder and Liquid Form.
- Shade of Cement – Universal shade.
Composition:
Powder
- Silica – 41.9%
- Alumina – 28.6 %
- Aluminum fluoride – 1.6%
- Calcium fluoride – 15.7%
- Sodium fluoride – 9.3%
- Aluminum Phosphate – 3.8 %
Liquid
- Polyacrylic acid – 35%
- Tartaric Acid – 5-15 %
- Water
Packaging
- 1 x Powder20g
- 1 x Liquid 15ml
Direction to Use
STEPS –
- Take powder liquid ratio 3:1
- Must be mixed within 45 sec.
- Use a polymer paper mixing pad for mixing the powder and liquid.
- Mix over a large area with a plastic spatula.
- Isolate the cavity.
- Apply calcium hydroxide liner.
- Condition the cavity wall properly.
- Bulk insertion of GIC.
- Complete it by doingFinishing and Polishing.
Precautions –
- Dispense the liquid just before mixing.
- Reseal the bottle immediately.
- Discard the last third of the liquid.
Warranty
- Warranty is not applicable for this product.