Sdi Wave Flowable Composite A1

Original price was: $ 10.24.Current price is: $ 8.10.

NANOFILLEDWave, Wave MV, and Wave HV contain specially treated nano-fillers to maximize polishability, wear-resistance and strength. Ease of extrusion is improved with the addition of these specially treated nano-fillers.FILLER LOADINGWave, Wave MV, and Wave HV all have excellent wear profiles due to their high filler loading level:FLOURIDE RELEASEFluoride?s cariostatic effect enhances remineralization and inhibits enamel demineralization. In an aqueous environment, the fluoride ions in Wave, Wave MV, and Wave HV diffuse from the resin into the surrounding tooth. This ionic movement is caused by oral fluid passing in and out of the resin and tooth, acting as a carrier for the fluoride ions.NATURAL FLORESCENCE?ave, Wave MV, and Wave HV contain a fluorescent agent that ensures perfectly natural-looking teeth under ultraviolet lights. No one will know!RADIOOPACITY?ave, Wave MV, and Wave HV are all visible on x-rays. This allows easy identification of secondary caries at the interface.COMPRESSIVE STRENGHTWave?s, Wave MV?s and Wave HV?s high compressive strength values expand the suitability for multiple applications.UDMAWave?s UDMA resin system minimizes shrinkage and reduces post-operative sensitivity.TIP LENGHT COMPARISIONWave?s complete tip length is 12.2mm, 40% longer than the alternative of 8.7mm. Wave?s longer tip length allows more direct placement of the material into difficult to reach areas.

Title	Quantity	Price
Bulk/tiered discount	2 - 5	1% $ 8.02
Bulk/tiered discount	6 - 10	2% $ 7.94
Bulk/tiered discount	11 - 20	4% $ 7.78
Bulk/tiered discount	21 - 50	5% $ 7.69
Bulk/tiered discount	51 +	7% $ 7.53

... people are viewing this right now

Features

NANOFILLED

Wave, Wave MV, and Wave HV contain specially treated nano-fillers to maximize polishability, wear-resistance and strength. Ease of extrusion is improved with the addition of these specially treated nano-fillers.

FILLER LOADING

Wave, Wave MV, and Wave HV all have excellent wear profiles due to their high filler loading level:

FLOURIDE RELEASE

Fluoride?s cariostatic effect enhances remineralization and inhibits enamel demineralization. In an aqueous environment, the fluoride ions in Wave, Wave MV, and Wave HV diffuse from the resin into the surrounding tooth. This ionic movement is caused by oral fluid passing in and out of the resin and tooth, acting as a carrier for the fluoride ions.

NATURAL FLORESCENCE?/strong>

Wave, Wave MV, and Wave HV contain a fluorescent agent that ensures perfectly natural-looking teeth under ultraviolet lights. No one will know!

RADIOOPACITY?/strong>

Wave, Wave MV, and Wave HV are all visible on x-rays. This allows easy identification of secondary caries at the interface.

COMPRESSIVE STRENGHT

Wave?s, Wave MV?s and Wave HV?s high compressive strength values expand the suitability for multiple applications.

UDMA

Wave?s UDMA resin system minimizes shrinkage and reduces post-operative sensitivity.

TIP LENGHT COMPARISION

Wave?s complete tip length is 12.2mm, 40% longer than the alternative of 8.7mm. Wave?s longer tip length allows more direct placement of the material into difficult to reach areas.

Description

Wave is the ideal versatile fluoride releasing, flowable, radiopaque, light cured composite. Wave is directly injected into the cavity preparation for maximizing adaptation to the preparation. The Wave shade range consists of 14 popular shades – enamel A1, A2, A3, A3.5, B1, B2, B3, C2, C3, D3, incisal, gingival, bleach; and 0A2 dentin shade. Enamel shades can be guided by VITA classical shade guide. Gingival shade is ideal for restoring cervical lesions in elderly patients. For teeth lighter than B1, bleach shade is available.

A choice of?/strong>3 viscosities-Wave,Wave MV (Medium Viscosity),Wave HV (High Viscosity) .?ave,?ave MV?nd?ave HV?/strong>contain specially treated?ano-fillers to?strong>maximize polishability,?ear resistance?nd?trength.?ase of extrusion is improved with the addition of these specially treated nano-fillers.

?strong>INDICATIONS:

Class V restorations
Tunnel/air abrasion preparations
Pit and fissure sealants
Minimal Class I, II, III, IV restorations
Radiopaque cavity liners
Cervical abrasion/erosion lesions
Abfraction lesions
Implant seals
Incisal abrasions
Repair enamel defects
Minor core build-ups
Temporary crowns
Cement porcelain/ceramic/ composite veneers
Splint mobile teeth
Attach fiber bridges
Restorations in deciduous teeth
Repair porcelain restorations
Block out undercuts in inlay/onlay/crown preparations
Cover stains
Adhering tooth jewelry
Ceramic inserts

?/p>

?DVANTAGE -?/strong>

Composite Wave is a very versatile fluid composite, making it suitable for most clinical situations.
Wave releases fluoride and protects against tooth decay.
It is radiopaque, so can be easily identified on x-rays.
It has very good resistance to compression, which increases its lifespan.
The wave includes a large quantity?f filling charge, which provides excellent wear resistance.
Low viscosity, light-cured, radiopaque flowable composite.
Flow on-demand handling.
Excellent Radiopacity.
Available in 14 shades including opaque and translucent.
No slumping and running.

?/p>

Key Specifications

COMPOSITION WAVE:

35% wt (52 Vol%) multifunctional methacrylic ester

65% wt (41 Vol%) (0.02 – 10 micron) inorganic filler

COMPOSITION WAVE MV:

40% wt (61 Vol%) multifunctional methacrylic ester

60% wt (39 Vol%) (0.02 – 10 micron) inorganic filler

COMPOSITION WAVE HV:

34% wt (53 Vol%) multifunctional methacrylic ester

66% wt (44 Vol%) (0.02 – 10 micron) inorganic filler?/p>

Packaging

1 x 1g Syringe

5 x disposable tips.

Direction of use

Clean and Isolate tooth. A conservative cavity should be prepared, employing standard techniques and instruments, to form a slightly rounded internal form. Margins of the cavity preparation should end in sound and supported enamel with no bevels in stress-bearing locations. If bevelling is desired in a low-stress location it should extend no further than 1mm at an angle of no greater than 45? Pre-wedging is also recommended to ensure that the restored tooth will have an adequate contact point. Prophy all surfaces to be etched including surfaces adjacent to the cavity with an oil free non-fluoride containing paste or a slurry of pumice and water. Rinse thoroughly with water.

SHADE SELECTION

Shade selection should be made with a just cleaned and moist tooth.

NOTE: Do not use uncured paste for color matching as there is a slight color change upon curing.

ISOLATION

Isolation techniques must be used to prevent contamination. A rubber dam is the preferred mode of isolation.

PULP PROTECTION

For deep cavities, use a calcium hydroxide liner and appropriate glass ionomer cement liner to protect deep cavity reparations in close proximity to the pulp.

1. Acid Etching

Thoroughly dry the surface to be etched with dry, oil-free air. Etch tooth surface with Super Etch 37% phosphoric acid.

(a) Enamel only Etch surface for at least 20 seconds

(b) Dentin and enamel Using the ?total-etch? technique etch the surface including any glass ionomer for at least 20 seconds. Enamel subjected to fluoridation should be etched for 90 to 120 seconds. Etching Precautions: Ensure that the dispensing tip hub is firmly attached to the syringe by twisting the hub securely onto the syringe. Avoid acid contact with oral tissues, eyes and skin. If accidental contact occurs wash thoroughly with water. In the case of eye contact, wash eye for 15 minutes and seek medical attention. Use matrix strips to protect adjacent tooth surfaces during etching. On first usage or after prolonged storage, extrude a small amount onto a mixing pad for familiarity with the etchant?s viscosity and rate of extrusion

2. Wash thoroughly with water

3. Remove excess water. Keep moist. Avoid contamination e.g. saliva

4. Apply Stae dentin/enamel adhesive to saturate all internal surfaces, or bonding agent according to manufacturer?s instructions

5. Blow gently with dry, oil-free air for 2 seconds to evaporate the solvent. Leave surface glossy

6. Light cure for 20 seconds (460-480nm wavelength, high power LED curing light)

7. Directly inject Wave in increments of 2mm or less in 7.1 Class V restorations, 7.2 Tunnel preparations, 7.3 Pit and fissures sealants, 7.4 Minimal Class I, Class II, Class III, and Class IV restorations. Or other indication as required.

CAUTION: Ensure that the dispensing tip is firmly attached to the syringe by twisting the tip hub securely onto the syringe.

1. We offer Worldwide Shipping by Courier via Air or Sea mode.
2. Product will be dispatched within 5-7 working days.
3. Delivery will take a maximum of 7-15 days, based on the shipping option you choose.
4. Kindly check customs restrictions and rules in your country for specific products, mostly 99% shipments are cleared and delivered smoothly.
5. For Bulk inquiries or customized manufacturing please contact us.

Product Enquiry

SKU: DK-11808 Categories: Dental Products, Medical Supplies, Restoratives Tags: Paedodontics, Sdi Wave Flowable Composite A1 Brand: SDI